优富® 树脂 CA500 YOUFU Resin CA500
|
|
|
|
外观 Appearance |
颗粒状 Granular |
|
供货颜色 Available Colors |
本色、黑色、定制色 Natural, Black, Customized |
|
供货区域 Supply Area |
中国、亚洲 China, Asia |
描述DESCRIPTION
高耐热高抗冲级PC/ABS CA500合金材料实现了超高缺口冲击强度与高耐热性的卓越结合，专为承受极端机械冲击、跌落及在较高温度环境下要求保持优异韧性的关键部件而设计。其综合性能满足了汽车、耐用电子设备及防护装备等领域对材料可靠性和耐用性的极高要求
The high heat resistance and high impact resistance PC/ABS CA500 alloy material achieves an excellent combination of ultra-high notch impact strength and high heat resistance, designed specifically for critical components that require excellent toughness to withstand extreme mechanical impacts, drops, and high temperature environments. Its comprehensive performance meets the extremely high requirements for material reliability and durability in fields such as automobiles, durable electronic devices, and protective equipment.
核心特性 / KEY FEATURES
- 超高抗冲击性: 室温缺口冲击强度高达70 KJ/m²，提供顶级的抗冲击和抗跌落保护。
Ultra high impact resistance: With a room temperature notch impact strength of up to 70 KJ/m ², it provides top-notch impact and drop protection.
- 高耐热性: 热变形温度（HDT@1.8MPa）达到111°C，确保零件在高温工况下的尺寸稳定性和结构完整性。
High heat resistance: heat deformation temperature（ HDT@1.8MPa ）Reaching 111 ° C ensures the dimensional stability and structural integrity of the parts under high temperature conditions.
- 良好的机械强度与刚性: 均衡的拉伸、弯曲强度及较高的弯曲模量，提供可靠的结构支撑。
Good mechanical strength and rigidity: balanced tensile and bending strength and high bending modulus, providing reliable structural support.
- 优异的综合韧性: 高冲击强度配合良好的断裂延伸率，材料在承受冲击时能有效吸收能量，防止脆性断裂。
Excellent comprehensive toughness: With high impact strength and good fracture elongation, the material can effectively absorb energy and prevent brittle fracture when subjected to impact.
典型应用 / TYPICAL APPLICATIONS
- 汽车内饰件及外饰功能件（如高要求卡扣、插接件、耐磨衬板）
Automotive interior and exterior functional parts (e.g., high-demand clips, connectors, wear-resistant liners).
- 通讯设备、高端消费电子及电动工具的外壳与结构件
Housings and structural parts for communication equipment, high-end consumer electronics, and power tools.
- 安全防护头盔外壳及关键承力部件
Shells and critical load-bearing components for safety helmets.
- 运动器材、行李箱等高强度耐冲击部件
High-strength, impact-resistant parts for sports equipment and luggage.
- 其他对材料韧性和耐热性有极端要求的工程部件
Other engineering components with extreme requirements for material toughness and heat resistance.
法规符合性 / REGULATORY COMPLIANCE
- 符合ROHS、REACH SVHC、CP65等法规要求。
- Compliant with regulations such asUL、 ROHS, REACH SVHC, CP65.
典型数据 / Typical data
|
项目 Project |
测试方法Test Method |
条件Condition |
单位Unit |
典型值Typical Value |
|
熔体流动速率 Melt Flow Rate |
ASTM D1238 |
240℃, 5.0 kg |
g/10min |
7 |
|
密度 Density |
ASTM D792 |
23℃ |
g/cm³ |
1.14 |
|
收缩率 Shrinkage |
ASTM D955 |
3.2 mm |
% |
0.4-0.6 |
|
拉伸强度 Tensile Strength |
ASTM D638 |
50 mm/min |
MPa |
560 |
|
断裂伸长率 Elongation at Break |
ASTM D638 |
50 mm/min |
% |
80 |
|
弯曲强度 Flexural Strength |
ASTM D790 |
2 mm/min |
MPa |
950 |
|
弯曲模量 Flexural Modulus |
ASTM D790 |
2 mm/min |
MPa |
28000 |
|
悬臂梁缺口冲击强度 Izod Impact, Notched |
ASTM D256 |
23℃, 3.2mm |
kJ/m² |
70 |
|
洛氏硬度 Rockwell Hardness |
ASTM D785 |
R 标尺 R Scale |
- |
114 |
|
热变形温度 Heat Deflection Temp |
ASTM D648 |
1.8 MPa, 6.4mm |
℃ |
111 |
|
阻燃等级 Flame Rating |
UL94 |
1.5 mm |
/ |
HB |
加工指南 / PROCESSING GUIDELINES
|
项目 Item |
条件/参数 Condition/Parameter |
|
干燥 Drying |
90-100℃, 3-4小时 hours |
|
料筒温度 Melt Temp. |
230-260℃ |
|
模具温度 Mold Temp. |
80-100℃ |
|
注射速度 Inj. Speed |
中等至高速 Medium to High |
|
背压 Back Pressure |
5-15 bar |
安全与免责声明 / SAFETY & DISCLAIMER
- 本资料所载数据为实验室典型值，仅供参考。实际性能可能因加工条件、产品设计及使用环境而异。
The data contained herein are laboratory typical values for reference only. Actual performance may vary depending on processing conditions, product design, and end-use environment.
- 使用者有责任根据自身具体应用进行充分测试和评估，以确保产品的适用性与安全性。
It is the user‘s responsibility to conduct sufficient testing and evaluation for their specific application to ensure product suitability and safety.
- 除非另有书面明确约定，本公司不对产品作任何明示或暗示的担保，并不承担由此产生的任何责任。
Unless otherwise expressly agreed in writing, our company makes no warranties, express or implied, and assumes no liability arising therefrom.